Ki sa ki chalè tretman pou alyaj 718?
Alyaj 718 (UNS N07718, W Nr 2.4668) yon austenitic nickel ki baze sou superalloy. Alloy 718 ekspozisyon excellent high-segren tensile ak creep rupture pwopriyete nan tanperati 1300 1300 degre F ak ekselan oxidation re ist;at tanperati 1800 degre F. Alloy 718 itilize nan aplikasyon mande fòs fòs%tankou jet jet motè pati ak gwo vitès avyon pati tankou wou yo, bokit, gaskets, ak -wo tanperati bolts ak tapi.
Tipik mekanik pwopriyete
Gen de de main kalite nan solisyon annealing ak aje tretman:
1)
Solisyon Trete (AMS 5662 Bar / AMS 5596 Fèy): 1725 degre F 7b{3}} degre F 2b 2b air refwadisman.
Heat Treatment (AMS 5663 Bar): 1325 degree F for 8 hours, cool to 1150 degree F at 100 degree F/hour, hold at 1150 degree F for 8 hours minutes, + air cooling.
Tretman bay pi wo a chanm tanperati tensile ak yield fòs ak pwodwi fatig fatig sa a Sa a !! optimal chalè tretman Alloy 718 kote a konbinezon nan fracture lavi, 2c 2c 2c fracture ak fracture ductility obligatwa.
2)
Altènativ solisyon tretman (AMS 5664 Bar / AMS 5597 Fèy): 1900 degre F 7b{3}} degre F + 2b cooling
Chalè Tretman: 1400 degre F 10 èdtan èdtan fouye 1200 degre F, èdtan èdtan total aje 1200 degre F 2b 2b lè refwadisman.
Sa a pi pito tretman in detire detire aplikasyon li pwodui optimal transverse ductility, enpak fòs, ak ba-tanperati notche tensile fòs epè sections. Severe, sa a tretman gen tendency pwodwi notch brittleness estrès fracture.