Segondè bon jan kalite ASTM B564 alyaj baton pou pwosesis pati nikleyè gaz incoloy 825 bar
Kòm yon founisè dirijan ak manifakti nan Lachin, GNEE Steel bay pri -nikèl-efikas pwodwi alyaj ki baze sou.
- Voye imèl -:ss@gneesteel.com
- Tel:+8615824687445
Non komen:
UNS N08825
Alloy 825
Nikèl 825
Estanda Egzekitif:
|
|
Fèy, plak, & dezabiye | Tib & tiyo |
|
BS 3076NA16 Asme SB 425 Asme SB 564 ISO 9725 ASTM B 425 ASTM B 564 ASME Code CASE N -572 DIN 17754 DIN 17752 ISO 9723 DIN 17753 Vdtüv 432 ISO 9724 |
BS 3072NA16 ASTM B 906 BS 3073NA16 ASTM B 424 Asme SB 424 Vdtüv 432 Asme SB 906 DIN 17750 ISO 6208 |
ASTM B 705 Asme SB 775 Asme SB 829 ASTM B 751 BS 3074NA16 ASTM B 704 ASTM B 775 ASME Kòd Ka 1936 ASTM B 163 Asme SB 423 Asme SB 704 ASME SB 705 ASTM B 829 Asme SB 163 Asme SB 751 ASTM B 423 DIN 17751 Vdtüv 432 ISO 6207 |
Incoloy 825 Pwopriyete Chimik:
| CHROMIUM (%) | 19.50 a 23.50 |
| Nikèl (%) | 38. 00 a 46. 00 |
| Titàn (%) | 0. 06 a 1.2 |
| Fè (%) | 22. 00 minimòm |
| Molibden (%) | 2.50 a 3.50 |
| Kabòn (%) | 0. 05 maksimòm |
| Copper (%) | 1.50 a 3. 00 |
| Souf (%) | 0. 03 maksimòm |
| Manganèz (%) | 1. 0 maksimòm |
| Aliminyòm (%) | 0. 2 maksimòm |
| Silisyòm (%) | 0. 5 Maksimòm |
Incoloy 825Pwopriyete mekanik:
| Fòs rupture (MPa) | Sede fòs (MPa) | Elongasyon (%) |
| 772 | 441 | 36 |
Incoloy 825 Pwopriyete fizik:
| Densite | Livr/nan3 | 0.294 |
| g/cm3 | 8.14 | |
| Koyefisyan ekspansyon tèmik (vle di) | Nan/ini degre f | 7.7 X 105 |
| Chalè espesifik | BTU/LB. degre f | 0.105 |
| J/kg • degre | 440 | |
| Tèmik konduktivite | BTU/H-FT- degre F | 6.4 |
| Modil Elastisite | KSI | 28.4 X 103 |
| MPA | 196 X 103 | |
| Pwen k ap fonn | oF | 2500 a 2550 |
| oC | 1370 a 1400 | |
| Pèmeyabilite | Nan 70oF | 200 |
Baj popilè: bon jan kalite segondè astm b564 alyaj baton pou pwosesis pati nikleyè gaz incoloy 825 bar, Lachin bon jan kalite segondè ASTM B564 alyaj baton pou pwosesis pati nikleyè gaz incoloy 825 founisè bar